Curing, Carbonation, Compressive strength, Mechanical properties, Ca(OH)2

Abstract

The increasing use of lime-based mortars for the restoration of historic buildings and structures justifies the research on these materials. The focus of this paper is the effect of technological variables on pore structure and mechanical properties of lime-based mortars. The influence of curing time, binder:aggregate ratio, aggregate attributes and porosity is discussed. Mortars prepared with aerial lime, varying aggregate types and binder:aggregate ratios ranging from (1:1) to (1:5) by volume were tested. Compressive and flexural strength measurements, as well as X-ray diffraction and thermal studies, were performed after 3, 7, 28, 91, 182 and 365 days. A strong increase in strength of mortar mixtures after 365 curing days (as compared to 28 curing days) is found. In spite of the fact that larger amounts of binder increase the total porosity, the strength of these mixtures is also increased. A good interlocked structure is obtained as binder contents increase. Also, higher porosities allow better portlandite carbonation. A relationship between mechanical properties and pore structure was established. However, in case of binder excess, the increase in voids leads to a strength reduction. The use of calcareous aggregates improves strength more as compared to the use of siliceous aggregates. Factors as grain size distribution and grain shape of the aggregates have also been considered.